A wave of layoffs that has swept the entire Internet industry has intensified. China's Internet industry has experienced several crises and major changes in the past development process. There is also a "brief history of layoffs by major Internet companies". Hot search, JD.com has a wide range of layoffs in this round of layoffs, and all its subsidiaries are involved. Most of the layoffs are between 10% and 20%. Among them, Jingxi Guangdong and other theaters have all laid off staff. Tencent also reported the news of downsizing and layoffs. Among them, Tencent PCG (Platform User Content Business Group) laid off 30% of its staff, iQiyi laid off 12% of its staff, Kuaishou was reported to have laid off 30% of its staff, and the e-sports department of Station B laid off 90% of its staff.
Mass layoffs on the internet have created a host of socioeconomic issues, including foam concrete.
The common problems of foamed concrete are bubbling, cracking, collapse, shrinkage, and other phenomena. To treat these phenomena, the proper medicine can be found, and the cause can be effectively solved.
The main reason for the collapse of foamed cement is that the cement solidification speed is too slow. We can solve this situation from the following aspects
1. Add accelerator to improve the setting time of foamed cement
Accelerators are used in more and more concrete applications. Foamed cement has high requirements for accelerators. It is not just a fast setting but also needs to be adapted to the performance of foamed cement, and accelerators cannot be added. After affecting the foaming situation.
2 Add an early strength agent to improve the early strength of foamed cement and reduce the stress generated during the exothermic process of cement hydration. Only when these two forces are balanced can it be ensured that the foamed cement will not crack and collapse in the later stage.
3. An appropriate amount of sulfoaluminate cement can be added, which many manufacturers choose to use in winter, and the cost performance is still relatively high. However, this amount of addition should also be paid attention to. It should not be added blindly. After many customers add sulfoaluminate cement, the finished product becomes very brittle in the later stage, without toughness, low strength, and severe pulverization. So we still have to adjust according to the current situation.
4 The water-cement ratio is not suitable. Collapse, retraction, bleeding, insufficient strength. To a large extent, it has something to do with the inappropriate water-cement balance. The adjustment of the water-cement ratio is a technical activity that requires trial and error. It has a lot to do with the cement of foamed cement and the fly ash aggregate, and it needs to be practiced repeatedly according to the actual situation. In this, we can add a plasticizer to adjust the water-cement ratio. This effect is very immediate.
The above contents are some solutions summed up by Tongrun according to the reasons for the collapse of foamed cement. If you encounter other problems or reasonable solutions in the actual process, you are also welcome to communicate us.
COVID-19 has led to many sites shutting down. What is the impact on China's foreign trade enterprises as a whole and small, medium and micro foreign trade enterprises?
. It is learned that some foreign trade enterprises have been affected by the epidemic and are facing periodic problems in foam concrete operated by foreign trade enterprises will also fluctuate with the changes of the epidemic. Contact us for the latest quotation on foam concrete.
Cerium nitride is known as CeN powder,Cerium nitride CeN powder is used in high-end ceramics, luminescent materials, special metallurgy.…
A hollow glass microsphere is a kind of hollow microsphere with a thin wall, high strength, and smooth surface…
Whether the cement used and the pumping agent are matched and adapted must be obtained through the adaptability test. The optimum amount of the pumping agent should be determined through the adaptability test with the cement cementitious material.…